Title: | A study on corrosion behavior of friction stir welded and tungsten inert gas welded AA2014 aluminium alloy |
Authors: | Sinhmar, Sunil |
Keywords: | Mechanical Engineering Aluminium Welding Pitting corrosion Polarization |
Issue Date: | Apr-2018 |
Publisher: | Elsevier |
Abstract: | The present study comprises the comparison of the electrochemical behavior of friction stir weld (FSW) joint and tungsten inert gas (TIG) weld joint of AA2014 using immersion test, potentiodynamic polarization test and electrochemical impedance spectroscopy (EIS). Weld thermal cycles and microhardness were correlated with corrosion behavior of the weld joints. TIG weld joint showed lower corrosion resistance than FSW joint. Heat affected zone was the most corrosion susceptible region in both type of weld joints. Optical microscopy, FESEM, TEM and XRD analysis were performed to discuss the corrosion behavior in light of the microstructure. |
URI: | https://www.sciencedirect.com/science/article/pii/S0010938X17315329#kwd0005 http://dspace.bits-pilani.ac.in:8080/jspui/xmlui/handle/123456789/15259 |
Appears in Collections: | Department of Mechanical engineering |
Files in This Item:
There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.