Title: Effect of Substrates on the Photoelectrochemical Reduction of Water over Cathodically Electrodeposited p-Type Cu2O Thin Films
Authors: Pande, Surojit
Keywords: Chemistry
Deposition
Thin films
Amorphous materials
Semiconductor photoelectrochemistry
Cathodic electrodeposition
Issue Date: 5-Aug-2015
Publisher: ACS
Abstract: In this study, we demonstrate development of p-Cu2O thin films through cathodic electrodeposition technique at constant current of 0.1 mA/cm2 on Cu, Al, and indium tin oxide (ITO) substrates from basic CuSO4 solution containing Triton X-100 as the surfactant at 30–35 °C. The optical and morphological characterizations of the semiconductors have been carried out using UV–vis spectroscopy, X-ray diffraction (XRD), scanning electron microscopy (SEM), and Raman spectroscopy. The band gap energy of ∼2.1 eV is recorded, whereas SEM reveals that the surface morphology is covered with Cu2O semiconductors. XRD analyses confirm that with change in substrate, the size of Cu2O “cubic” crystallites decreases from ITO to Al to Cu substrates. Photoelectrochemical characterizations under dark and illuminated conditions have been carried out through linear sweep voltammetry, chronoamperometry and electrochemical impedance spectroscopic analysis. The photoelectrochemical reduction of water (H2O → H2) in pH 4.9 aqueous solutions over the different substrates vary in the order of Cu > Al > ITO. The highest current of 4.6 mA/cm2 has been recorded over the Cu substrate even at a low illumination of 35 mW/cm2, which is significantly higher than the values (2.4 mA/cm2 on Au coated FTO or 4.07 mA/cm2 on Cu foil substrate at an illumination of 100 mW/cm2) reported in literature.
URI: https://pubs.acs.org/doi/abs/10.1021/acsami.5b04116
http://dspace.bits-pilani.ac.in:8080/xmlui/handle/123456789/3448
Appears in Collections:Department of Chemistry

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.