Abstract:
In order to prepare a suitable oxide based solid electrolyte for Li+ ion batteries, Li+ NASICON LATP nanocrystallites [LiAl0.3Ti1.7(PO4)3] have been externally dispersed in fast ionic oxide glassy system, viz, 60[Li2SO4]-40[Li2O-P2O5]. To prepare this novel composite, milling assisted synthesis route was adopted in which ionic glass and LATP were separately ball milled, subsequently mixed and pelletized. The present work reports that even for a very small amount of LATP (1 wt%) in the mixture, the conductivity exhibits a significant enhancement. Structural and electrical properties of the composite with a typical composition of 1%(LATP)-99%(60LSLP) have been reported. X-ray diffraction confirmed that milling leads to reduction in the size of both the glass grains and the LATP crystallites. These novel composites have been found to be potential candidates for all solid-state battery applications