Department of Chemical Engineering
Permanent URI for this collectionhttp://localhost:4000/handle/123456789/1923
Browse
2 results
Search Results
Item Aluminium terephthalate (Al-BDC) based metal organic framework decorated carboxymethylated filter cloth for defluoridation application(Elsevier, 2023-06) Chatterjee, SomakCurrent work adopts a novel approach for deposition of aluminium terephthalate-based metal organic framework (MOF) on carboxymethylated filter paper for defluoridation purpose. Aluminium terephthalate-based MOF was prepared using an optimized technique and showed a fluoride uptake capacity of 665 mg/g. However, due to its low yield, synthesized MOF was immobilized on carboxymethylated filter paper, using hydrothermal method. MOF immobilized filter paper (MOF cloth) showed a fluoride uptake capacity of 88 mg/g. Different surface-based characterization for MOF and MOF cloth were performed. Synthesized MOF was quasi-spherical in shape, forming flower like structures, when coalesced together and it showed crystalline property, having lattice fringes of 0.2 nm. Uniform and dense distribution was observed during its deposition process on filter paper. Both functional groups and mineralogical phases present in the MOF were also imparted to the immobilized filter paper. Uptake of fluoride by MOF cloth was governed by monolayer adsorption, as evident from Langmuir isotherm analysis. Uptake capacity increased with temperature and the highest one was recorded at 318 K. Prepared MOF cloth was subjected to dynamic studies via glass-funnel based filtration, where, effects of pH, coexisting ions including an organic pollutant and real-life feed were carried out. Regeneration of the MOF cloth was also studied for four cycles. Leaching study was performed at different time intervals. Finally, comparison was made with different conventional MOF based adsorbents and it was observed that this cloth can be an adaptable and pollution free medium for defluoridation applications.Item Polyacrylonitrile and polyethersulfone based co-axial electrospun nanofibers for fluoride removal from contaminated stream(Elsevier, 2024-02) Chatterjee, SomakCoaxial electrospun polyacrylonitrile (PAN) and polyethersulfone (PES) based nanofibers were prepared and was used for filtration of fluoride from drinking water for the first time. Well defined fiber geometry was obtained at 1 ml/h of core polymer, i.e., PES flow rate, 1.4 ml/h of shell polymer, i.e., PAN flow rate, voltage of 22 kV, while the distance between the needle tip and the collector was 15–17 cm. Increase in bead like structure in fiber strands was observed with higher PAN concentration, while it decreased for lower PES concentration, thereby giving an optimum composition (6 wt% PAN and 10 wt% PES) for uniform fiber morphology. This nanofiber, abbreviated as N2 acted as an ultrafiltration membrane having permeability in the lower range, i.e., 0.5 × 10−11 m/s Pa and its fluoride removal efficacy was 46%. Fibers were also hydrophilic with considerable porous nature. Uptake of fluoride by this N2 nanofibers were evident from binding energy of 685.2 eV during XPS analysis. It is probable that nitrile and sulfone groups present in the core and shell of the nanofibers played an active in fluoride uptake, which was estimated as 110 mg/g at 298 K. Isoelectric point was in alkaline range which promoted negative fluoride ion uptake on positive nanofiber surface. Lead played higher masking effect in the uptake of fluoride in comparison to arsenic as coexisting ion. Dynamic cross flow filtration was also studied with this nanofiber in both synthetic and real life feed solution.